"CrystalSystem" "Temperature" "E<sub>g</sub>" "IsCalculated" "ReferenceId" "Comment" "StructureType" "SpaceGroup" "Modification" "Amorphous" "300" "0.4" "0" "27" "Film" "" "" "" "Cubic" "" "1.11" "0" "30" "Optical" "Diamond" "Fd3m" "" "Cubic" "" "1.11" "0" "31" "Optical" "Diamond" "Fd3m" "" "Cubic" "0" "1.15" "0" "37" "" "Diamond" "Fd3m" "" "Cubic" "0" "1.153" "0" "37" "" "Diamond" "Fd3m" "" "Cubic" "0" "1.17" "0" "30" "" "Diamond" "Fd3m" "" "Cubic" "0" "1.17" "0" "31" "" "Diamond" "Fd3m" "" "Cubic" "0" "1.21" "0" "27" "" "Diamond" "Fd3m" "" "Cubic" "0" "1.21" "0" "28" "" "Diamond" "Fd3m" "" "Cubic" "0" "1.21" "0" "50" "" "Diamond" "Fd3m" "" "Cubic" "1.8" "1.1695" "0" "31" "" "Diamond" "Fd3m" "" "Cubic" "4.2" "1.1558" "0" "31" "" "Diamond" "Fd3m" "" "Cubic" "291" "1.1135" "0" "31" "" "Diamond" "Fd3m" "" "Cubic" "295" "1.107" "0" "37" "" "Diamond" "Fd3m" "" "Cubic" "298" "1.11" "0" "72" "Indirect transition" "Diamond" "Fd3m" "" "Cubic" "298" "1.12" "0" "72" "Indirect transition" "Diamond" "Fd3m" "" "Cubic" "298" "1.14" "0" "72" "Indirect transition" "Diamond" "Fd3m" "" "Cubic" "298" "1.15" "0" "72" "Indirect transition" "Diamond" "Fd3m" "" "Cubic" "298" "1.17" "0" "72" "Indirect transition" "Diamond" "Fd3m" "" "Cubic" "298" "3.43" "0" "72" "Direct transition" "Diamond" "Fd3m" "" "Cubic" "300" "1.08" "0" "37" "" "Diamond" "Fd3m" "" "Cubic" "300" "1.1" "0" "27" "" "Diamond" "Fd3m" "" "Cubic" "300" "1.2" "0" "27" "Film" "Diamond" "Fd3m" "" "Cubic" "300" "1.2" "0" "27" "Single crystal" "Diamond" "Fd3m" "" "Cubic" "1685" "0.6" "0" "31" "" "Diamond" "Fd3m" "" "Monoclinic" "" "1.551" "1" "1540" "Calculation. CASTEP" "" "P2/m" "J"

Chart

X axis: Y axis:

CSV Viewer: Si

CrystalSystem Temperature Eg IsCalculated ReferenceId Comment StructureType SpaceGroup Modification
Amorphous 300 0.4 0 27 Film
Cubic 1.11 0 30 Optical Diamond Fd3m
Cubic 1.11 0 31 Optical Diamond Fd3m
Cubic 0 1.15 0 37 Diamond Fd3m
Cubic 0 1.153 0 37 Diamond Fd3m
Cubic 0 1.17 0 30 Diamond Fd3m
Cubic 0 1.17 0 31 Diamond Fd3m
Cubic 0 1.21 0 27 Diamond Fd3m
Cubic 0 1.21 0 28 Diamond Fd3m
Cubic 0 1.21 0 50 Diamond Fd3m
Cubic 1.8 1.1695 0 31 Diamond Fd3m
Cubic 4.2 1.1558 0 31 Diamond Fd3m
Cubic 291 1.1135 0 31 Diamond Fd3m
Cubic 295 1.107 0 37 Diamond Fd3m
Cubic 298 1.11 0 72 Indirect transition Diamond Fd3m
Cubic 298 1.12 0 72 Indirect transition Diamond Fd3m
Cubic 298 1.14 0 72 Indirect transition Diamond Fd3m
Cubic 298 1.15 0 72 Indirect transition Diamond Fd3m
Cubic 298 1.17 0 72 Indirect transition Diamond Fd3m
Cubic 298 3.43 0 72 Direct transition Diamond Fd3m
Cubic 300 1.08 0 37 Diamond Fd3m
Cubic 300 1.1 0 27 Diamond Fd3m
Cubic 300 1.2 0 27 Film Diamond Fd3m
Cubic 300 1.2 0 27 Single crystal Diamond Fd3m
Cubic 1685 0.6 0 31 Diamond Fd3m
Monoclinic 1.551 1 1540 Calculation. CASTEP P2/m J