Materials Library Visualization

"CrystalSystem" "SpaceGroup" "E<sub>g</sub>" "IsCalculated" "ReferenceId" "Comment" "Modification" "StructureType" "Temperature" "Monoclinic" "C2/c" "0.05" "1" "895" "Indirect. Calculation. CALYPSO method; 0.3 GPa" "" "" "" "Monoclinic" "C2/c" "0.06" "1" "895" "Indirect. Calculation. CALYPSO method; 2 GPa" "" "" "" "Monoclinic" "C2/m" "0.17" "1" "895" "Indirect. Calculation. CALYPSO method; 4.9 GPa" "" "" "" "Cubic" "F4(-)3m" "1.1" "0" "33" "" "&alpha;" "CaF<sub>2</sub>" "" "Cubic" "F4(-)3m" "1.1" "0" "50" "" "&alpha;" "CaF<sub>2</sub>" "300" "Cubic" "F4(-)3m" "1.3" "0" "27" "" "&alpha;" "CaF<sub>2</sub>" "300" "Cubic" "F4(-)3m" "1.3" "0" "36" "" "&alpha;" "CaF<sub>2</sub>" "300" "Cubic" "F4(-)3m" "1.3" "0" "40" "" "&alpha;" "CaF<sub>2</sub>" "300" "Cubic" "Fm3m" "1.2" "0" "37" "" "&beta;" "CaF<sub>2</sub>" "300" "Cubic" "Fm3m" "1.29" "0" "37" "" "&beta;" "CaF<sub>2</sub>" "300" "Cubic" "Fm3m" "1.5" "0" "27" "" "&beta;" "CaF<sub>2</sub>" "300" "Cubic" "Fm3m" "1.7" "0" "37" "" "&beta;" "CaF<sub>2</sub>" "300" "Cubic" "Fm3m" "0.25" "0" "50" "" "&beta;" "CaF<sub>2</sub>" "993"

Chart

X axis: Y axis:

CSV Viewer: Cu2Se

CrystalSystem SpaceGroup Eg IsCalculated ReferenceId Comment Modification StructureType Temperature
Monoclinic C2/c 0.05 1 895 Indirect. Calculation. CALYPSO method; 0.3 GPa
Monoclinic C2/c 0.06 1 895 Indirect. Calculation. CALYPSO method; 2 GPa
Monoclinic C2/m 0.17 1 895 Indirect. Calculation. CALYPSO method; 4.9 GPa
Cubic F4(-)3m 1.1 0 33 α CaF2
Cubic F4(-)3m 1.1 0 50 α CaF2 300
Cubic F4(-)3m 1.3 0 27 α CaF2 300
Cubic F4(-)3m 1.3 0 36 α CaF2 300
Cubic F4(-)3m 1.3 0 40 α CaF2 300
Cubic Fm3m 1.2 0 37 β CaF2 300
Cubic Fm3m 1.29 0 37 β CaF2 300
Cubic Fm3m 1.5 0 27 β CaF2 300
Cubic Fm3m 1.7 0 37 β CaF2 300
Cubic Fm3m 0.25 0 50 β CaF2 993