"CrystalSystem" "E<sub>g</sub>" "IsCalculated" "ReferenceId" "Temperature" "StructureType" "SpaceGroup" "Comment"
"Cubic" "3.1" "0" "30" "" "" "" ""
"Cubic" "3.115" "0" "32" "4.2" "" "" ""
"Cubic" "2.8" "0" "37" "300" "" "" ""
"Cubic" "3.047" "0" "581" "80" "sphalerite" "F4(-)3m" "Optical absorption spectroscopy. Excitonic transition. Thin film, polycristalline"
"Cubic" "3.07" "0" "581" "300" "sphalerite" "F4(-)3m" "Estimation. Direct transition. Single crystal"