Materials Library Visualization
"Modification" "CrystalSystem" "StructureType" "SpaceGroup" "E<sub>g</sub>" "IsCalculated" "ReferenceId" "Comment" "Temperature"
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "0.93" "0" "27" "Optical" ""
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "0.93" "0" "37" "Optical" ""
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "0.96" "0" "27" "" ""
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "0.96" "0" "37" "" ""
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "1" "0" "27" "Optical" ""
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "1" "0" "30" "Optical" ""
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "1" "0" "33" "Optical" ""
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "1.1" "0" "27" "" ""
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "1.1" "0" "33" "" ""
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "0.86" "0" "27" "" "0"
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "0.86" "0" "30" "" "0"
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "0.86" "0" "581" "Thermal activation. Polycristalline" "0"
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "1.1" "0" "36" "" "0"
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "0.96" "0" "36" "" "0"
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "1" "0" "36" "" "0"
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "1.11" "0" "33" "" "5"
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "1.09" "0" "33" "" "80"
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "1.1" "0" "33" "" "100"
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "0.93" "0" "581" "Optical absorption spectroscopy. Single crystal" "297"
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "0.51" "0" "581" "Optical absorption spectroscopy. Thin film, polycristalline" "300"
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "0.93" "0" "27" "" "300"
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "0.98" "0" "33" "" "300"
"α" "Tetragonal" "Zn<sub>3</sub>P<sub>2</sub>" "P4<sub>2</sub>/nmc" "1" "0" "33" "" "300"
Chart
X axis:
Y axis:
CSV Viewer: Zn3As2
| Modification | CrystalSystem | StructureType | SpaceGroup | Eg | IsCalculated | ReferenceId | Comment | Temperature |
|---|---|---|---|---|---|---|---|---|
| α | Tetragonal | Zn3P2 | P42/nmc | 0.93 | 0 | 27 | Optical | |
| α | Tetragonal | Zn3P2 | P42/nmc | 0.93 | 0 | 37 | Optical | |
| α | Tetragonal | Zn3P2 | P42/nmc | 0.96 | 0 | 27 | ||
| α | Tetragonal | Zn3P2 | P42/nmc | 0.96 | 0 | 37 | ||
| α | Tetragonal | Zn3P2 | P42/nmc | 1 | 0 | 27 | Optical | |
| α | Tetragonal | Zn3P2 | P42/nmc | 1 | 0 | 30 | Optical | |
| α | Tetragonal | Zn3P2 | P42/nmc | 1 | 0 | 33 | Optical | |
| α | Tetragonal | Zn3P2 | P42/nmc | 1.1 | 0 | 27 | ||
| α | Tetragonal | Zn3P2 | P42/nmc | 1.1 | 0 | 33 | ||
| α | Tetragonal | Zn3P2 | P42/nmc | 0.86 | 0 | 27 | 0 | |
| α | Tetragonal | Zn3P2 | P42/nmc | 0.86 | 0 | 30 | 0 | |
| α | Tetragonal | Zn3P2 | P42/nmc | 0.86 | 0 | 581 | Thermal activation. Polycristalline | 0 |
| α | Tetragonal | Zn3P2 | P42/nmc | 1.1 | 0 | 36 | 0 | |
| α | Tetragonal | Zn3P2 | P42/nmc | 0.96 | 0 | 36 | 0 | |
| α | Tetragonal | Zn3P2 | P42/nmc | 1 | 0 | 36 | 0 | |
| α | Tetragonal | Zn3P2 | P42/nmc | 1.11 | 0 | 33 | 5 | |
| α | Tetragonal | Zn3P2 | P42/nmc | 1.09 | 0 | 33 | 80 | |
| α | Tetragonal | Zn3P2 | P42/nmc | 1.1 | 0 | 33 | 100 | |
| α | Tetragonal | Zn3P2 | P42/nmc | 0.93 | 0 | 581 | Optical absorption spectroscopy. Single crystal | 297 |
| α | Tetragonal | Zn3P2 | P42/nmc | 0.51 | 0 | 581 | Optical absorption spectroscopy. Thin film, polycristalline | 300 |
| α | Tetragonal | Zn3P2 | P42/nmc | 0.93 | 0 | 27 | 300 | |
| α | Tetragonal | Zn3P2 | P42/nmc | 0.98 | 0 | 33 | 300 | |
| α | Tetragonal | Zn3P2 | P42/nmc | 1 | 0 | 33 | 300 |