"CrystalSystem" "SpaceGroup" "E<sub>g</sub>" "IsCalculated" "ReferenceId" "Temperature" "Direction" "StructureType" "Comment"
"Tetragonal" "P4<sub>2</sub>/mnm" "3.97" "0" "30" "" "" "" ""
"Tetragonal" "P4<sub>2</sub>/mnm" "0.72" "0" "37" "300" "" "" ""
"Tetragonal" "P4<sub>2</sub>/mnm" "1.5" "0" "37" "300" "" "" ""
"Tetragonal" "P4<sub>2</sub>/mnm" "3.54" "0" "27" "300" "" "" ""
"Tetragonal" "P4<sub>2</sub>/mnm" "3.54" "0" "29" "300" "" "" ""
"Tetragonal" "P4<sub>2</sub>/mnm" "3.54" "0" "30" "300" "" "" ""
"Tetragonal" "P4<sub>2</sub>/mnm" "3.596" "0" "34" "4" "(-)χ" "" ""
"Tetragonal" "P4<sub>2</sub>/mnm" "3.99" "0" "34" "4" "||c" "" ""
"Tetragonal" "P4<sub>2</sub>/mnm" "3.597" "0" "581" "1.8" "" "Rutile" "Optical absorption spectroscopy. Direct transition. Single crystal"
"Tetragonal" "P4<sub>2</sub>/mnm" "2.6" "0" "581" "77" "" "Rutile" "Indirect transition"
"Tetragonal" "P4<sub>2</sub>/mnm" "2.45" "0" "581" "300" "" "Rutile" "Optical absorption spectroscopy. Indirect transition. Thin film, polycristalline"
"Tetragonal" "P4<sub>2</sub>/mnm" "3.54" "0" "581" "300" "" "Rutile" "Optical absorption spectroscopy. Thin film, polycristalline"
"Tetragonal" "P4<sub>2</sub>/mnm" "3.71" "0" "581" "300" "" "Rutile" "Optical absorption spectroscopy. Single crystal"
"Tetragonal" "P4<sub>2</sub>/mnm" "3.9" "0" "581" "300" "" "Rutile" "Diffuse reflectance spectroscopy. Polycristalline"
"Tetragonal" "P4<sub>2</sub>/mnm" "4.3" "0" "581" "300" "" "Rutile" "Optical absorption spectroscopy. Thin film, polycristalline"
"Tetragonal" "P4<sub>2</sub>/mnm" "3.631" "0" "581" "0" "⊥c" "Rutile" "Optical absorption spectroscopy. Thin film, single crystal"
"Tetragonal" "P4<sub>2</sub>/mnm" "2.55" "0" "581" "300" "⊥c" "Rutile" "Optical absorption spectroscopy. Indirect transition. Thin film, polycristalline"
"Tetragonal" "P4<sub>2</sub>/mnm" "2.7" "0" "581" "300" "⊥c" "Rutile" "Optical absorption spectroscopy. Indirect transition. Thin film, polycristalline"
"Tetragonal" "P4<sub>2</sub>/mnm" "3.57" "0" "581" "300" "⊥c" "Rutile" "Diffuse reflectance spectroscopy. Single crystal"
"Tetragonal" "P4<sub>2</sub>/mnm" "3.69" "0" "581" "300" "⊥c" "Rutile" "Optical absorption spectroscopy. Single crystal"
"Tetragonal" "P4<sub>2</sub>/mnm" "3.7" "0" "581" "300" "⊥c" "Rutile" "Optical absorption spectroscopy. Single crystal"
"Tetragonal" "P4<sub>2</sub>/mnm" "3.947" "0" "581" "0" "||c" "Rutile" "Optical absorption spectroscopy. Thin film, single crystal"
"Tetragonal" "P4<sub>2</sub>/mnm" "3.93" "0" "581" "300" "||c" "Rutile" "Diffuse reflectance spectroscopy. Single crystal"
"Tetragonal" "P4<sub>2</sub>/mnm" "4.1" "0" "581" "300" "||c" "Rutile" "Optical absorption spectroscopy. Single crystal"
Chart
X axis:
Y axis:
CSV Viewer: SnO2
| CrystalSystem | SpaceGroup | Eg | IsCalculated | ReferenceId | Temperature | Direction | StructureType | Comment |
|---|---|---|---|---|---|---|---|---|
| Tetragonal | P42/mnm | 3.97 | 0 | 30 | ||||
| Tetragonal | P42/mnm | 0.72 | 0 | 37 | 300 | |||
| Tetragonal | P42/mnm | 1.5 | 0 | 37 | 300 | |||
| Tetragonal | P42/mnm | 3.54 | 0 | 27 | 300 | |||
| Tetragonal | P42/mnm | 3.54 | 0 | 29 | 300 | |||
| Tetragonal | P42/mnm | 3.54 | 0 | 30 | 300 | |||
| Tetragonal | P42/mnm | 3.596 | 0 | 34 | 4 | (-)χ | ||
| Tetragonal | P42/mnm | 3.99 | 0 | 34 | 4 | ||c | ||
| Tetragonal | P42/mnm | 3.597 | 0 | 581 | 1.8 | Rutile | Optical absorption spectroscopy. Direct transition. Single crystal | |
| Tetragonal | P42/mnm | 2.6 | 0 | 581 | 77 | Rutile | Indirect transition | |
| Tetragonal | P42/mnm | 2.45 | 0 | 581 | 300 | Rutile | Optical absorption spectroscopy. Indirect transition. Thin film, polycristalline | |
| Tetragonal | P42/mnm | 3.54 | 0 | 581 | 300 | Rutile | Optical absorption spectroscopy. Thin film, polycristalline | |
| Tetragonal | P42/mnm | 3.71 | 0 | 581 | 300 | Rutile | Optical absorption spectroscopy. Single crystal | |
| Tetragonal | P42/mnm | 3.9 | 0 | 581 | 300 | Rutile | Diffuse reflectance spectroscopy. Polycristalline | |
| Tetragonal | P42/mnm | 4.3 | 0 | 581 | 300 | Rutile | Optical absorption spectroscopy. Thin film, polycristalline | |
| Tetragonal | P42/mnm | 3.631 | 0 | 581 | 0 | ⊥c | Rutile | Optical absorption spectroscopy. Thin film, single crystal |
| Tetragonal | P42/mnm | 2.55 | 0 | 581 | 300 | ⊥c | Rutile | Optical absorption spectroscopy. Indirect transition. Thin film, polycristalline |
| Tetragonal | P42/mnm | 2.7 | 0 | 581 | 300 | ⊥c | Rutile | Optical absorption spectroscopy. Indirect transition. Thin film, polycristalline |
| Tetragonal | P42/mnm | 3.57 | 0 | 581 | 300 | ⊥c | Rutile | Diffuse reflectance spectroscopy. Single crystal |
| Tetragonal | P42/mnm | 3.69 | 0 | 581 | 300 | ⊥c | Rutile | Optical absorption spectroscopy. Single crystal |
| Tetragonal | P42/mnm | 3.7 | 0 | 581 | 300 | ⊥c | Rutile | Optical absorption spectroscopy. Single crystal |
| Tetragonal | P42/mnm | 3.947 | 0 | 581 | 0 | ||c | Rutile | Optical absorption spectroscopy. Thin film, single crystal |
| Tetragonal | P42/mnm | 3.93 | 0 | 581 | 300 | ||c | Rutile | Diffuse reflectance spectroscopy. Single crystal |
| Tetragonal | P42/mnm | 4.1 | 0 | 581 | 300 | ||c | Rutile | Optical absorption spectroscopy. Single crystal |